Tips for Offshore Wind Corrosion Protection

Corrosion protection is always the last step during a production process. When a job is behind schedule, there is often pressure on the paint shop to make up for lost time by hastening its part of the production process. But trying to gain time by rushing the painting process can have costly consequences.

Painting offshore structures in a paint shop costs from €15 to €25 per m², depending on the setup of the workshop and the paint system. The cost of coating repair work performed on site and onshore is about 5 to 10 times more, due to the logistics of getting men and materials to the job site and limited access to structures due to weather conditions. If repair work must be done offshore, when corrosion protection fails prematurely, the cost can increase to more than €1000/m2, between 40 and 60 times the cost of doing the job in the paint shop.

Onshore exposure implies generally cyclic dew/condensation, with or without minor salinity, and moderate exposure to sunlight, resulting in moderate corrosion at holidays, weak points and damaged areas of the coating system. In contrast, offshore exposure implies long-term exposure to humidity with high salinity, intensive influence of UV light, wave action and the presence of a splash zone area, and high corrosive stress resulting in speedy corrosion at vulnerable areas of the coating system.

This difference in exposure severity is also reflected in the mass and thickness loss per unit surface of low-carbon steel and zinc in the first year of their unprotected exposure. For example, in Germany, the onshore corrosivity is evaluated as being about C3, according to ISO 12944, which corresponds to a thickness loss of 25 to 50 μm. In comparison, for splash zone areas, as much as 500 μm thickness loss has been observed in the first year of service.

Key factors for corrosion protection

A qualified coating system is not enough to guarantee a successful corrosion protection. Certificates and approvals are often overestimated. Indeed, the EN ISO 12944, part 5 (German issue) lists nine factors that are decisive for the durability of a coating system. The coating system itself is only one, and other important factors include the design of the structure (access possibilities), the design of edges and weld seams, the workmanship of the applicator, the specific condition of the steel before surface preparation, and the exposure of the paint system immediately after completing application.

In effect, failure statistics show that the paint system itself is seldom the reason for the premature failure of the corrosion protection. The paint industry is mainly supplying 'half-products': that is, two or more component-reactive resins. It is the applicator who effectively creates a chemically new substance that in the end provides corrosion protection. Failure can occur during this process if the mixing of the components, the temperature control, the time requirements, and the application of the mixture onto correctly prepared surfaces are not all carried out properly. That is why permanent quality control and supervision by qualified professionals are required.

Design considerations

The design and fabrication of steel used in wind turbine construction is critical to its corrosion protection. Before the applicator starts their job, the steel builder has to provide a structure suited to being painted successfully. It is a law of nature that corrosion will always start at edges and weld seams – which is where the responsibility of the steel builder begins.

Coatings can only protect accessible surfaces – a fact often neglected in design. EN ISO 12944, part 3, Design Considerations, recommends that appropriate distances required for tools in corrosion protection work are respected. It also recommends minimum dimensions for openings that provide access to confined areas, minimum dimensions for narrow spaces between surfaces, and the incorporation of design features that may be used to avoid deposits accumulating or water being trapped.

Construction designs that create insufficient access for painting should be avoided. During the fabrication of an offshore steel structure, the recommendations of ISO 8501, part 3 (preparation grades of welds, edges, and other areas with surface imperfections) should also be considered. This relatively new standard, which appears not to be well known at engineering offices and steel construction companies, is aimed at the steel builder, not the paint applicator. It gives recommendations about the required condition of the steel surface if paints are to be applied later for long-term corrosion protection.

For offshore structures, preparation grades P2 or P3 should be specified, depending on the relevant details of the structure. This means the steel surface should be free from welding spatters and slags, pores, undercuts and laminations. The surface also needs to be dressed (by grinding) to remove irregular and sharp-edged profiles.


Performance testing an offshore corrosion protection system on WindFloat, a semi-submersible floating structure for offshore wind turbines that has been deployed with a 2 MW Vestas turbine off the Portuguese coast (Hempel)

Pores are often found, particularly on welds, and inspectors are often asked if pores can be filled up with paint. Pores should never be filled with paint or filler. The steel builder has to repair them, according to the demands of EN ISO 5813, weld quality B.

Correctly designed weld seams are crucial to successful corrosion protection. Handmade weld seams on offshore structures generally need to be ground by the steel fabricator before they can be painted. Poor weld seam design will cause steel to corrode quickly.

It is often helpful to have something to show to the welder to clarify what is meant by the right design for corrosion protection at a weld seam. The NACE Standard RP 0178, for example, provides photographic examples of the front and back sides of good and bad weld seams.

Finally, the steel fabricator has to be careful about the condition of the carbon steel to be used to build an offshore structure. Unpainted steel is characterised by four rust grades according to EN ISO 8501, part 1. For offshore structures, it is strongly recommended to use steel with a rust grade not worse than B (Norsok M501), or not worse than C (EN ISO 12944). The service life of a coating system depends directly on the rust grade of the initial steel and the degree of surface preparation (Sa2 and Sa3 according to EN ISO 8501, part 1).

In summary, the steel fabricator has to be aware that he is constructing an offshore structure that needs certain access and surface conditions for successful corrosion protection.

Surface preparation and paint application

The workmanship of the applicator is very important for a coating system's long service life. Half of all premature corrosion protection failures are application-related; thus all operations must be high quality and quality control checks must be frequent. Correct surface preparation and coating thickness are definitely the most important application parameters. Planning and informing the work crew of the different procedures and, preferably, signing off on the results are necessary to guarantee the right level of quality.


Because offshore structures present some of the toughest corrosion protection challenges for coating systems, the best possible equipment and setup should always be used for painting. Automatic blast facilities should be used to minimise variations in surface cleanliness and surface roughness. Painting booths with climate control and temperature regulation are recommended.

Two-component spray equipment should be used to minimise mixing errors. The foreman and/or supervisor should be qualified and certified according to FROSIO or NACE level 3 or equivalent.

The coating system

Today more than ever, the market for corrosion protection of steel wind turbine towers is typified by strong competition. Coating application around the clock, under time pressure, carried out by foreign workers with whom communicating can be difficult, are typical aspects of a day of coating work. Demand is increasing for fast-drying, solvent-free coatings, lower thicknesses, and in addition there is a need for fewer coats.

In reality, successful testing and certification for coating systems do not necessarily guarantee successful coating performance. Indeed, it is one thing to apply the very best coating under laboratory conditions onto perfectly prepared test panels and submit the panels for laboratory testing.

Offshore structures present some of the toughest corrosion protection challenges for coating systems (Hempel)

Replicating the same results on site, on thousands of square metres of steel, applied around the clock and sometimes under less than optimal conditions, is a completely different matter. The more difficult a coating system is to apply, the higher the requirements during application, and consequently the more challenging the task of the paint applicator.

Coating materials should, therefore, not only be easy to apply, but should also, to some extent, be versatile enough to tolerate the variations in application that occur in daily practice.

Field experience matters

Nothing says more about the quality and performance of a coating system than field experience. Such experiences offshore say much more than any tests ever can.

Only practical experience can demonstrate whether the coating system can be reliably applied daily at different locations, at different temperatures, during all seasons, onto different structures, onto complicated geometry, with low spray dust pickup, with good flow properties, good sag resistance and good thickness tolerances. And, furthermore, only practical experience will tell whether a coating system can even be reliably repaired on-site using standard methods.

However, while long-term experience with a company is the most reliable basis for coating selection when going offshore with its coating solutions, new, unproven coating systems will always be required by an offshore wind industry in constant evolution.

Anders Voldsgaard Clausen is group wind power segment manager at Hempel A/S



Renewable Energy Finance

Clean Energy ETFs Are on a Tear

Eric Balchunas, Bloomberg Green investing used to be synonymous with losing money. But while the S&P 500 Index is up 2 percent this year, and the MSCI All-Country World Index is up 5 percent, clean energy ETFs have double-digit re...

Wheels, Towers and Trees: Unconventional Renewable Energy Technologies in the Pipeline

Andrew Williams, International Correspondent A number of companies around the world are developing novel technologies in an effort to grab a slice of the global renewable energy market.  Although many of these technologies are simple incremental improvements to e...
UK Parliament Clean Energy Leaders

UK Government Names Clean Energy Cabinet Members

David Appleyard, Contributing Editor With the UK general election now over and a majority Conservative Party government in place, the re-elected Prime Minister David Cameron has now named key members of the government charged with steering the UK’s clean energ...

Coast to Coast and Across the Electric System, Microgrids Provide Benefits to All

Dick Munson, Environmental Defense Fund At the most obvious level, microgrids could disrupt today’s utilities and their regulated-monopoly business model, because they challenge the centralized paradigm. In a nutshell, microgrids are localized power grids that ha...


Volume 18, Issue 3


To register for our free
e-Newsletters, subscribe today:


Tweet the Editors! @megcichon @jennrunyon



Doing Business in Brazil – in partnership with GWEC, the Global Win...

Brazil is one of the most promising markets for wind energy.  Ranke...

Energy Storage USA 2015

Energy Storage USA is the leading conference in the United States focuse...

Wind Power Central America

Wind power projects are expected to reach 46GW of total installed capaci...


SunEdison Expands Residential Market Offerings with New PPA, Sales ...

SunEdison has largely focussed on the commercial and utility-scale solar...

Are You Ready for a Natural Disaster?

Guest post by Jenna Clarke  Living in the Shenandoah Valley of Virg...

Deadline for Inclusion in Solar Power World's Top Solar Contractors...

UPDATE: The official deadline for the Solar Power World T...


Renewable Energy: Subscribe Now

Solar Energy: Subscribe Now

Wind Energy: Subscribe Now

Geothermal Energy: Subscribe Now

Bioenergy: Subscribe Now